Glass flake mortar has excellent corrosion resistance, which is mainly concerned with the mastic composition. In general, anti-corrosion layer of corrosion failures are mainly a resin substrate by etching, the base resin is first generated weight loss, color change, etc., after the material causing bubbling, delamination, peeling or cracking, etc., leading to failure of the anti-corrosion layer , especially the latter, due to factors such as penetration, accelerated corrosive chemical medium is infiltrated into the inside of the protective layer. Therefore, the choice has good corrosion resistance of the resin matrix, it should also take effective measures to weaken, slow penetration of corrosive media or water vapor. The VEGF flake mortar than the matrix resin can provide more effective corrosion resistance, mainly because the glass flakes VEGF can effectively prevent corrosion of the physical media or water vapor permeation. Glass flake clay has a strong anti-permeability is related to its material composition, under normal circumstances, VEGF flake clay tablets containing 10% -40% diameter ranging from glass flakes, clay, after construction is completed, the flat glass flakes in resin continuous phase was parallel overlapping arrangement to form a dense barrier layer structure. Corrosive media in the cured cement after penetration must undergo countless tortuous pathway, so corrosion-resistant layer of a certain thickness, the corrosion penetration distance greatly extended, corresponds to an effective increase in the thickness of the corrosion layer on the objective. Meanwhile, in the absence of glass flake reinforced, the resin matrix continuous phase there will be a lot of so-called "defects" such as pores, bubbles and other micro-joints, etc. The presence of these defects will accelerate the corrosion process or accelerate penetration of the medium, because once medium penetrate into these defects, the rate of penetration is improved at the same time, the area of ??contact with corrosive media matrix continuous phase also will be increased, thereby further accelerating the physical penetration and chemical etching processes, whereas in VEGF glass flake clay, since the parallel arrangement of the glass flakes can effectively dividing the matrix resin of the continuous phase "defects", which can effectively suppress the permeation rate of a corrosive medium. Features Uses: glass flake production of heavy-duty coatings, pearlescent pigments and plastics indispensable raw material, used in the field of preservation, can significantly improve the corrosion resistance of the coating to extend the life of the object; pearlescent pigments used to make glass flake pearlescent pigments The gloss is far superior to natural mica, synthetic mica pearlescent pigment production, and both anti-corrosion, anti-ultraviolet radiation functions; for the field of plastics, plastic products, increase strength and prevent precision parts made of thermoplastics thermal deformation, increase its dimensional stability. 1, the glass flakes can prevent water vapor and solvent on the substrate material chemical erosion. The extent of the substrate or coating with chemical resistance of the glass material chosen varies, the glass flakes by C- glass composition having excellent chemical durability. 2, due to the relative and steel, cement and other base material larger coefficient of elongation, so in the case of thermal shock and cracking of the resin layer is likely to fall off, and the glass flakes can commission a thermally stable layer, thus preventing the cleavage of the substrate and flaking. 3, good heat resistance. The use of glass flake lining heat resistance than similar resin coating can increase 20-40 ℃, so commonly used in oil pipelines, water pipelines, chemical resistant devices. 4, the thermal expansion coefficient. 5, the coating containing the glass flakes stiff than without glass flake epoxy or polyester resin layer, it is highly resistant to surface wear properties. 6, good compatibility properties, can be composed of a variety of anti-corrosion coatings and resins. Features: 1, glass flake can prevent water vapor and chemical solvents on the base material erosion. The extent of the substrate or coating with chemical resistance of the glass material chosen varies, the glass flakes by C- glass composition having excellent chemical durability. 2, due to the relative and steel, cement and other base material larger coefficient of elongation, so in the case of thermal shock and cracking of the resin layer is likely to fall off, and the glass flakes can commission a thermally stable layer, thus preventing the cleavage of the substrate and flaking. 3, good heat resistance. The use of glass flake lining heat resistance than similar resin coating can increase 20-40 ℃, so commonly used in oil pipelines, water pipelines, chemical resistant devices. 4, the thermal expansion coefficient. 5, the coating containing the glass flakes stiff than without glass flake epoxy or polyester resin layer, it is highly resistant to surface wear properties. 6, good compatibility properties, can be composed of a variety of anti-corrosion coatings and resins.